PA6 Established ET6000-5021 X7 GREY PolyOne Corporation Nylon 6

Item No.: ET6000-5021 X7 GREY
PA6, also known as nylon 6, is a translucent or opaque milky white granule. It is thermoplastic, lightweight, tough, chemical and durable. It is commonly used in automotive parts, mechanical parts, electronic parts

       Melting point: 210 - 220 °C De
INQUIRY
Description
Basic characteristics of molding considerations

The chemical and physical properties of PA6 are similar to those of PA66. However, it has a low melting point and a wide process temperature range. Its impact resistance and resistance

Solubility is better than PA66, but it is also more hygroscopic. Since many of the quality characteristics of plastic parts are affected by hygroscopicity, the PA6 design is used.

Consider this when considering products. In order to improve the mechanical properties of PA6, various modifiers are usually added. Fiberglass is the most common

Additives are sometimes added to synthetic rubbers such as EPDM and SBR to improve impact resistance. For products without additives, shrinkage of PA6

Between 1% and 1.5%. The addition of a glass fiber additive reduces the shrinkage to 0.3% (but slightly higher in the direction perpendicular to the flow).

The shrinkage of the molded component is primarily affected by the crystallinity and hygroscopicity of the material. The actual shrinkage is also related to the design of the plastic part, the wall thickness and other process parameters.

Functional relationship.

The difference between PA6 and PA66

PA6 product properties Melting point: 210 - 220 °C Decomposition temperature: > 300 °C Flash point: > 400 °C Auto-ignition temperature: > 450 °C Physical state: Solid particle odor: Non-toxic: No recovery: Can be finally treated: Soil ( Harmless) Industrial waste) Extinguishing media: Various extinguishing agents (water, foam, powder, CO2, sand) can be used. Transportation: Non-dangerous goods, suitable for all types of transport vehicles. European Community Standard: Performance of non-dangerous PA66 products

Melting point: 250-270°C Decomposition temperature: > 350°C Flash point: > 400°C Auto-ignition temperature: > 450°C Physical state: Solid particle odor: Non-toxic: No recovery: Final treatment: Soil (harmless industrial waste) Extinguishing media: Various fire extinguishing agents (water, foam, powder, carbon dioxide, sand) can be used. Transportation: Non-dangerous goods, suitable for all types of transport vehicles. European Community Standard: Non-Dangerous Goods

Fold edit this paragraph application range
It is widely used in industrial production, manufacturing bearings, circular gears, cams, bevel gears, various rollers, pulleys, pump impellers, fan blades, worm gears,

Propellers, screws, nuts, washers, high pressure seals, oil resistant gaskets, oil resistant containers, housings, hoses, cable jackets, scissors

Pulley sleeves, bullfighting planing rails, electromagnetic dispensing valve seats, cold air equipment, gaskets, bearing cages, various tubing on cars and tractors,

Pistons, ropes, drive belts, textile machinery industry equipment, zero fog, daily necessities and packaging films.

Processing Technology
Drying treatment:

Since PA6 is easy to absorb moisture, special attention should be paid to drying before processing. If the material is supplied with waterproof material, then the capacity is

The device should be kept sealed. If the humidity is greater than 0.2%, it is recommended to dry in hot air above 80 °C for 16 hours. If the material is already in the air

Dew time is more than 8 hours, it is recommended to vacuum dry at 105 ° C for more than 8 hours.

Melting point temperature:

230-280 ° C, suitable for 250-280 ° C enhanced varieties




PA6 Japan Mitsubishi: 33% glass fiber reinforced flame retardant grade 1016G-33;
PA6 Japan Sansan: 30% glass fiber reinforced flame retardant grade 1013G-30, 1016G-30;
PA6 Japan Mitsubishi: 20% glass fiber reinforced flame retardant grade 1013G-20;
PA6 Japan Mitsubishi: 16% glass fiber reinforced flame retardant grade 1013G-16, 1016G-16;
PA6 Japan Ube: extrusion grade 1030B; standard viscosity 1013B, 1013NW8;
PA6 BASF Germany: glass fiber reinforced B3WG3, B36EG3; 30% glass fiber reinforced B3WG6;
PA6 Germany BASF: 30% glass fiber reinforced tape stabilizes B3WG6, B3EG6;
PA6 Germany BASF: 16% glass fiber reinforced tape stabilizes B3EG3; injection molding grade B3S;
PA6 Germany BASF: C36, B3WM602;
PA6 Germany Bayer: injection molding grade B30S; 30% glass fiber reinforced grade BKV130 (plating);
PA6 Taiwan Jisheng: injection molding grade TP-4407, 6203;
PA6 Switzerland EMS: BG-26, 30S, PV-6HH;
PA6 Netherlands DSM: 33% glass fiber reinforced grade K224-G6, K224-PG3
 
Physical Properties Metric English Comments
Density  1.24 g/cc 0.0448 lb/in³ ISO 1183
 
Mechanical Properties Metric English Comments
Hardness, Shore A  96 96 ISO 868
Hardness, Shore D  50 50 ISO 868
Tensile Strength, Ultimate  50.0 MPa 7250 psi 200 mm/min; DIN 53504
Tensile Stress   15.0 MPa
@Strain 100 %
2180 psi
@Strain 100 %
200 mm/min; DIN 53504
  31.0 MPa
@Strain 300 %
4500 psi
@Strain 300 %
200 mm/min; DIN 53504
Elongation at Break  420 % 420 % 200 mm/min; DIN 53504
Rebound  30 % 30 % Resilience; ISO 4662
Tear Strength  120 kN/m 685 pli 500 mm/min; ISO 34-1
Abrasion  30 30 mm³, Method A; ISO 4649
Compression Set   25 %
@Temperature 23.0 °C
25 %
@Temperature 73.4 °F
72 hr; ISO 815
  50 %
@Temperature 70.0 °C
50 %
@Temperature 158 °F
24 hr; ISO 815
 






Review