Item No.: C216V30
PA6 Excellent strength and toughness, meeting the mechanical properties of structural components; Excellent heat resistance, continuous use at temperatures up to 130 ° C; Long-term fatigue resistance, good performance after heat aging; Excellent dimension
INQUIRY
Description
The chemical and physical properties of PA6 are similar to those of PA66. However, it has a low melting point and a wide process temperature range.
It has better impact resistance and solubility resistance than PA66, but it is also more hygroscopic. Because of the many quality characteristics of plastic parts
It is subject to hygroscopicity, so take this into account when designing your product with PA6. To improve
The mechanical properties of PA6 are often added to a wide variety of modifiers. Glass is the most common additive, sometimes for
To improve impact resistance, synthetic rubbers such as EPDM and SBR are also added.
For products without additives, PA6 shrinks between 1% and 1.5%. Adding fiberglass additives can make
The shrinkage is reduced to 0.3% (but slightly higher in the direction perpendicular to the flow). The shrinkage rate of molding assembly is mainly
Affected by the crystallinity and hygroscopicity of the material.


Product Name: Polyamide 6 or Nylon 6 (PA6)

 Properties: translucent or opaque milky white crystalline polymer
 Features: thermoplastic, lightweight, tough, chemical and durable
 Combustion identification method: blue yellow flame, burning plant flavor
 Solvent test: cyclohexanone resistant and aromatic solvents
 Density: (g/cm3) 1.14-1.15
 Balanced water absorption: 3.5%
 Has good wear resistance, self-lubricating and solvent resistance.
 Tensile strength: > 60.0Mpa
 Elongation rate: > 30%
 Bending strength: 90.0Mpa
 Notched impact strength: > 5 (KJ/m2)



Conditional content
Injection pressure
Usually between 750 and 1250 bar, depending on the material and product design. PA66 environmental fiber

Injection speed
High speed (slightly lower reinforcement).
Runners and gates: Due to the short settling time of the PA66, the location of the gate is very important. The gate aperture should not be less than 0.5 * t (where t is the thickness of the plastic part).

Introduction to physics and chemistry
PA6 plastic material is a translucent or opaque milky white or yellow granular crystalline polymer with plasticity. Density (g / cm3) 1.10-1.14; tensile strength (MPa) 60.0-80.0; Rockwell hardness 118; melting point 252 ° C; embrittlement temperature -30 ° C; thermal decomposition temperature greater than 350 ° C continuous heat resistance 80-120 °C; impact strength (kJ / m2) 60-100; static bending strength (MPa) 1 00-120; Martin heat (°C) 50-60; flexural modulus (MPa) 2000~3000; volume resistivity (Ωcm ) 1.83 × 1015; equilibrium water absorption rate of 2.5%; dielectric constant of 1.63.
Chemical formula: [-NH(CH2)6-NHCO(CH2)4CO] n corrosion-resistant acid, alkali, most inorganic salt solution, alkyl halide, ester, ketone, etc.
PA66 has a higher melting point in polyamide materials. In product design, the shrinkage of PA66 is between 1% and 2%.
Today, a variety of disposable nozzles are used in the market to modify the physical properties of raw materials. At the same time, the price is cheaper than raw materials, which saves customers a lot of cost. Chemical Co., Ltd. is a company specializing in the production of modified granules and enjoys a high reputation in the local area.


Application information is
Widely used in the manufacture of machinery, automotive, chemical and electrical components such as gears, rollers, pulleys, rollers, pump impellers, fan blades, high pressure seals, valve seats, gaskets, bushings, various handles, support frames, internal lines Package, etc.

Conditional content
Injection pressure
Depending on the material and product design, it is usually between 750 and 1250 bar. PA66 environmental fiber

PA6 established Nymax X GMF 604 40 UV black glass fiber 30% wear-resistant nylon 66 plastic material flow channel

And Gates: Because of the short set-up time of the PA66, the position of the door is very important. The gate aperture should not be less than 0.5 * t (where t is the thickness of the plastic part).

Introduction to Physics and Chemistry
PA66 plastic material is a translucent or opaque milky white or yellow granular crystalline polymer with plasticity. Density (g / cm3) 1.10-1.14; tensile strength (MPa) 60.0-80.0; Rockwell hardness 118; melting point 252 ° C; embrittlement temperature -30 ° C; thermal decomposition temperature greater than 350 ° C, continuous heat resistance 80- 120 ° C; impact strength (kJ / m2) 60-100; static bending strength (MPa) 1 00-120; Martin heat (°C) 50-60; flexural modulus (MPa) 2000 ~ 3000; volume resistivity ( Ωcm) 1.83×1015; equilibrium water absorption is 2.5%; dielectric constant is 1.63.
Chemical formula: [-NH(CH2)6-NHCO(CH2)4CO] n corrosion-resistant acid, alkali, most inorganic salt solution, alkyl halide, ester, ketone, etc.
PA66 has a higher melting point in polyamide materials. In product design, PA66 shrinks between 1% and 2%.
At present, there are various disposable nozzles on the market for modification, and the physical properties of the raw materials can also be achieved. At the same time, the price is cheaper than raw materials, saving a lot of costs for customers. Chemical Co., Ltd. is a company specializing in the production of modified granules and enjoys a high reputation in the local area.





​​​​​​​